Salt spray fog ageing of hybrid composite/metal rivet joints for automotive applications
2017
Abstract The present experimental investigation aims to investigate the effect of salt-fog exposition on the mechanical behaviour of composite/metal riveted joints. To this aim, two kinds of joint were exposed to salt-fog environmental conditions according to ASTM B117 standard, for fifteen weeks. In particular, two composite laminates (i.e. glass fibre and carbon fibre/epoxy composites) were used as composite substrate joined with the metal substrate (i.e. aluminium alloy Al 6060). Single-lap shear tests were carried out in order to evaluate the evolution of the mechanical performances and the damage mechanisms of the riveted joints during the ageing exposition. The results evidence that t…
Effect of external basalt layers on durability behaviour of flax reinforced composites
2016
Abstract Aim of this work is to evaluate the influence of external layers of basalt-mat on the durability behaviour of flax reinforced epoxy composites. To this scope, long-term ageing tests were performed on two different laminates in critical environmental conditions. The first laminate, named Flax, was constituted by stacking ten layers of bidirectional flax fabrics. The second one, named Flax–Basalt, was produced by replacing two external flax layers with two layers of basalt mat for each side of the laminate. Both laminates were exposed to salt-fog environmental conditions, according to ASTM B 117 standard, for 60 days. Five samples per laminate were removed from salt-fog spray chamber…
Pull-off adhesion of hybrid glass-steel adhesive joints in salt fog environment
2016
The aim of this paper was to evaluate the durability behaviour of glass/steel adhesive joints exposed to salt fog environmental conditions for ten weeks, according to ASTM B117 standard. To this scope, pull-off mechanical tests were carried out in order to evaluate the performances evolution and damage phenomena of the adhesive joints during the ageing exposition. Two different types of adhesives were compared (i.e. epoxy and polyurethane ones). Moreover, the effects of the glass surface condition and the presence of a basalt mat layer within the adhesive thickness were evaluated. The mechanical performances were related with the occurred failure mechanisms. Epoxy-based joints showed higher…
DOMESTIC MATERIAL CONSUMPTION INDICATOR AND NATURAL RESOURCES: A EUROPEAN ANALYSIS OF THE ENVIRONMENTAL KUZNETS CURVE
2014
The study investigates the relation between per capita Domestic Material Consumption indicator (DMC) and per capita income. Economic literature focuses mainly on air, water and land pollution while we consider as environmental degradation the consumption on natural resources extracted from the environment. Using a cross– European panel of countries over the period 2000-2011, our results confirm the absence of an Environmental Kuznets Curve (EKC) between per capita DMC and per capita GDP both for EU-27 vs. 30 European countries and for Western vs. Eastern European countries. The turning points are so high that it is present a monotonic increasing relation between DMC indicator and GDP.
Durability of Basalt/Hemp Hybrid Thermoplastic Composites
2019
The Achilles heel of thermoplastic natural fibre composites is their limited durability. The environmental degradation of the mechanical properties of hemp and hemp/basalt hybrid-reinforced high-density polyethylene (HDPE) composites has been investigated with a special focus on the effects of water ageing and accelerated ageing, including hygrothermal and UV radiation. Modification of the matrix was carried out using a maleic anhydride high-density polyethylene copolymer (MAPE) as a compatibilizer. Hybridization of hemp fibres with basalt fibres and the incorporation of MAPE were found to significantly decrease the water uptake (up to 75%) and increase the retention of mechanical propertie…
On the response of flax fiber reinforced composites under salt-fog/dry conditions: Reversible and irreversible performances degradation
2022
Abstract Despite their scarce resistance to humid or wet conditions, natural fiber reinforced composites (NFRCs) seem to be able to partially recover their performances under discontinuous exposition to marine environment. To investigate this peculiarity, flax fiber reinforced composite was at first subjected to salt-fog spray condition at 35 °C for 15 and 30 days, respectively, and then stored in ‘‘dry” condition (i.e., 50% R.H. and 22 °C) between 0 and 21 days. The performances evolution was evaluated through flexural tests, water uptake and contact angle measurements. Moreover, the morphology of fractured mechanical samples was examined by using 3D optical microscope and scanning electro…
Durability behavior of bio-epoxy/jute-basalt hybrid composites for cladding
2016
The technology of dry assembly to produce multi-layer panels is an efficient alternative to traditional systems. Eco-sustainable systems are increasingly studied, particularly fiber reinforced composites for external cladding, based on natural fibers. However, the durability of these composites gives serious concern, in particular for their potential use in outdoor applications. To overcome this drawback, hybridization of natural fibers with mineral fibers as basalt ones appears promising. In this paper, the aging resistance of jute-reinforced laminate was compared with those of two hybrid laminates.
Effects of aging in salt spray conditions on flax and flax/basalt reinforced composites: Wettability and dynamic mechanical properties
2016
Abstract In the last years, the industrial policies are more attentive to issues concerning sustainability, recycling and environmental care. Therefore, the use of natural fibres in composite materials has spread more and more. This paper deals with flax and basalt fibres within an epoxy matrix by investigating the wettability and the dynamic mechanical properties of the resulting composites, subjected to long-term aging tests in critical environmental conditions. The first laminate was constituted by stacking ten layers of bidirectional flax fabrics. The second one was produced by replacing two external flax layers with two layers of basalt mat, for each side of the laminate. Both laminate…
Bilayer biodegradable films prepared by co-extrusion film blowing: Mechanical performance, release kinetics of an antimicrobial agent and hydrolytic …
2020
Abstract Bilayer biodegradable, eco-friendly films were prepared by co-extrusion film blowing, coupling polylactic acid (PLA) and Bio-flex ® (BIO). Furthermore, in the PLA layer, carvacrol (CRV) was added as a natural antimicrobial additive, whereas a nanoclay (D72T) was integrated to protect CRV from volatilization and to modulate release. The materials were analyzed by morphological, chemical-physical, mechanical testing. Furthermore, CRV release and degradation tests were performed. The results pointed out that coupling the two matrices allows gathering the stiffness of PLA with the ductility of BIO. Furthermore, the interlayer adhesion is promoted by CRV. D72T exerts a key-role in avoid…
Effect of hydrothermal ageing on the thermal and delamination fracture behaviour of CFRP composites
2014
Abstract This work investigates the hydrothermal ageing behaviour of a carbon fibre reinforced laminate and its epoxy matrix in bulk conditions. A model DGEBA epoxy is employed, and water uptake and dynamic mechanical thermal (DMTA) analyses have been performed on both the composites and bulk resin. Fracture toughness of the bulk resin has been measured, evidencing a substantially unmodified critical stress intensity factor KIC, although the evidence of plasticisation effects given by DMTA. Interlaminar Mode I fracture toughness of the composite showed a variable trend towards slight decreases or slight increases, according to the prevailing toughening or embrittling mechanisms activated by…